Influence of manufacturing process on the strength of composite materials

Boris Fedulov, Daria Bondarchuk, Alexey Fedorenko

    Результат исследований: Вклад в журналСтатья конференциирецензирование

    Аннотация

    Residual stresses in laminated composites induced by non-uniform matrix solidification and shrinkage through manufacturing process may lead to the shape distortion and possible damage of the final product. In this work, the phase transition model for matrix material was numerically implemented into Abaqus software to simulate evolution of stiffness properties and development of residual stresses of composite laminate during manufacturing temperature cycle. This simulation shows the presence of significant residual stresses in composites even before mechanical processing of the material. As an example, the residual stresses were computed for the plate with cross-ply layup. As a last step two specimens with presence of residual stresses and without one were loaded up to failure using progressive damage model. Modelling results show essential influence of residual stresses on distribution and development of matrix cracks, failure modes and strength values.

    Язык оригиналаАнглийский
    Страницы (с-по)541-548
    Число страниц8
    ЖурналProcedia Manufacturing
    Том37
    DOI
    СостояниеОпубликовано - 2019
    Событие9th International Conference on Physical and Numerical Simulation of Materials Processing, ICPNS 2019 - Moscow, Российская Федерация
    Продолжительность: 10 окт. 201915 окт. 2019

    Fingerprint

    Подробные сведения о темах исследования «Influence of manufacturing process on the strength of composite materials». Вместе они формируют уникальный семантический отпечаток (fingerprint).

    Цитировать