Cement grains with surface-synthesized carbon nanofibres: Mechanical properties and nanostructure

Petr Hlavacek, Vit Smilauer, Pavel Padevet, Larisa Nasibulina, Albert G. Nasibulin

Результат исследований: Глава в книге, отчете, сборнике статейМатериалы для конференциирецензирование

8 Цитирования (Scopus)

Аннотация

The carbon nanotubes were synthetized directly on the surface of Portland cement particles. Mixing this new carbon/cement material with ordinary cement creates a modified cementitious substance, where carbon is perfectly dispersed in the volume. In presented work, the fracture energy and compressive strength of cement paste/mortar created from this new material was measured. The composites with weight fractions of carbon nanotubes/paste in the ranges 0-0.038 were prepared and mechanically tested. Slight increase in fracture energy and compressive strength was observed even in the low carbon weigh fraction 0.019.

Язык оригиналаАнглийский
Название основной публикацииNANOCON 2011 - Conference Proceedings, 3rd International Conference
ИздательTANGER Ltd.
Страницы75-80
Число страниц6
ISBN (электронное издание)9788087294277
СостояниеОпубликовано - 2011
Опубликовано для внешнего пользованияДа
Событие3rd International Conference NANOCON 2011 - Brno, Чехия
Продолжительность: 21 сент. 201123 сент. 2011

Серия публикаций

НазваниеNANOCON 2011 - Conference Proceedings, 3rd International Conference

Конференция

Конференция3rd International Conference NANOCON 2011
Страна/TерриторияЧехия
ГородBrno
Период21/09/1123/09/11

Fingerprint

Подробные сведения о темах исследования «Cement grains with surface-synthesized carbon nanofibres: Mechanical properties and nanostructure». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать